Lincoln Electric Excalibur 11018M MR - Manual

Excalibur
®
11018M MR ™
Publication C2.10.1 10/06
www.lincolnelectric.com
STICK
Basic, Low Hydrogen, Low Alloy Steel SMAW Electrode
(AWS E11018M-H4R)
Excalibur ® 11018M MR ™ is designed primarily for joining high strength steel types in the as-
welded or stress relieved conditions with excellent low temperature impact properties and
robust welding procedures. All-position welding, except vertical down.
Advantage Lincoln
Integrated Silicate Technology™
Increased moisture resistance and decreased coating fragility.
Easy Strike™ Tip
Consistent, smooth arc starts.
Square Burn-Off
Focused arc for hard to access welds.
X-Ray Quality
Demanding applications.
Hermetically Sealed Packaging – Easy Open Cans
Delivers quality product, performance reliability and
consistent results.
ISO 9001 and 14001 Certified
Manufactured to standards for environmental and quality
management systems.
Welding Positions
Conformance
AWS A5.5/A5.5M:2006 E11018M-H4R / E7618M-H4R
ASME SFA 5.5:1996 E11018M-H4R
CSA W48-01: E7618-M-H4
DIAMETERS / LENGTH / PACKAGING
Diameter Length 10 Lb. (4.5 kg) 50 Lb. (22.7 kg)
in. (mm) in. (mm) Easy Open Can Easy Open Can
3/32 (2.4) 14 (350) ED031972 ED031975
1/8 (3.2) 14 (350) ED031973 ED031976
5/32 (4.0) 14 (350) ED031974 ED031977
3/16 (4.8) 14 (350) ED031978
1G 2F 2G 3G ➔
4G
%C %Mn %Si %P %S %Ni %Cr %Mo %V
Requirements
0.10 max 1.30 - 1.80 0.6 max 0.030 max 0.030 max 1.25 - 2.50 0.40 max 0.25 - 0.50 0.05 max
AWS E11018M-H4R
Test Results 0.04 - 0.05 1.55 - 1.80 0.40 - 0.55 0.010 - 0.030 0.005 - 0.020 1.90 - 2.50 0.02 - 0.15 0.35 - 0.50 0.005 - 0.015
DEPOSIT COMPOSITION – As required per AWS A5.5/A5.5M:2006
Charpy V-Notch Diffusible
Tensile Strength Yield Strength Elongation ft*lbf (Joules) Hydrogen
psi (MPa) psi (MPa) % @-60°F (-50°C) ml/100g
Requirements 110 (760) 98 - 110 20 20 (27) ≤4
AWS E11018M-H4R min. (680 - 760)
Test Results 111 - 117 100 - 110 20-25 40 - 65 1-4
As-welded (765 - 807) (690 - 758) (54 - 88)
MECHANICAL PROPERTIES – As Required per AWS A5.5/A5.5M:2006
TYPICAL OPERATING PROCEDURES
Polarity Current Range (Amps)
3/32 in. 1/8 in. 5/32 in. 3/16 in.
(2.4 mm) (3.2 mm) (4.0 mm) (4.8 mm)
DC+ 70-110 90-160 130-210 180-300
Typical Applications
• Certain Weldable Quenched & Tempered Steels, such as
- T1, A514, A517 and A709
• General Fabrication Requiring E11018-G or E11018M
Electrode Classification.
1F
6G ➔ 5G ➔ 4F
3F ➔