Operation, B-18 – Lincoln POWER-ARC 4000 User Manual

Page 33

Advertising
background image

B-18

OPERATION

B-18

POWER-ARC 4000

4. The bead should be put on with a weaving motion,

and it should be 1/2-3/4” (12.7-19.0mm) wide. Do
not let the arc blow over the edge, as that will dull
the edge. (See drawing below.)

5. Use the back-stepping method. Begin to weld 3”

(76mm) from the heel of the share and weld to the
heel. The second weld will begin 6” (152mm) from
the heel, the third weld 9” (229mm) from the heel,
etc.

Backstepping greatly reduces the chances for crack-
ing of the share, and it also greatly reduces warping.

NOTE: The entire process is rather fast. Many begin-
ners go much too slowly when hardfacing plowshares,
running the risk of burning through the thin metal.

Welding Cast Iron

When welding on a piece of cold cast iron, the
tremendous heat from the arc will be absorbed and
distributed rapidly into the cold mass. This heating
and sudden cooling creates WHITE, BRITTLE cast
iron in the fusion zone. (See drawing below.)

This is the reason why welds in cast iron break.
Actually, one piece of the broken cast iron has the
entire weld on it and the other piece has no weld on it.
(See drawing below.)

To overcome this, the welding operator has two
choices:

1. Preheat the entire casting to 500-1200°F (260-

649°C). If the cast iron is hot before welding, there
will be no sudden chilling which creates brittle
white cast iron. The entire casting will cool slowly.

2. Weld 1/2” (12.7mm) at a time, and do not weld at

that spot again until the weld is cool.

This way, no large amount of heat is put into the
mass.

Most inexperienced welders will probably use the sec-
ond method, because they have no way of preheating
large castings. Smaller castings can easily (and
should) be preheated before welding. A forge, stove,
fire, or the Arc Torch are all excellent means of pre-
heating.

When using the 1/2” (12.7mm) at a time method, it is
recommended to start 1/2” (12.7mm) away from the
previous bead and weld into the previous bead. This
is called backstepping.

After welding Cast Iron, protect the casting against
fast cooling. Put it in a container of warm, dry sand or
lime.

If sand or lime is not available, cover it with sheet
metal or any other non-flammable material that will
diminish drafts and retain heat.

Cast Iron Plate Preparation

Wherever practical, the joint to be welded should be
“veed” out by grinding or filing to give complete pene-
tration as shown in figures (a), (b) and (c) below. This
is especially important on thick castings where maxi-
mum strength is required.

Work Table

Strike Arc
Here

Sharp Edge

Weaving Motion

Plow Share

Positioning of Share

Brick

1/2-3/4" width
(12-20mm)

hot

cold

cold

White brittle
cast iron

When breaking
the weld stays on
one piece

First weld from A to B; then
from C to A; then from D to C;
then from E to D; and so on.

BACKSTEPPING

(75mm)

3"

B

A

C

D

E