Carbolite VST 17/-- - Manual (Page 7)

1700° Tube
LMF32C – 1.07 7
2.12 Tube Life
A ceramic work tube may crack if workpieces are inserted
too quickly or at temperatures below 900°C (when the tube
is more brittle). Large pieces should also be heated slowly
to ensure that large temperature differences do not arise.
Poor thermal contact should be encouraged between the
workpiece and the tube; crucibles or boats should be of
low thermal mass and should have feet to reduce the
contact with the tube (fig. 4).
Avoid metal directly touching the work tube - see the safety warning above.
Do not set too high a heating rate. Large diameter tubes are more susceptible to thermal shock
than smaller. A general rule for maximum heating rate is 400/internal diameter (°C/min); for
75mm i/d tubes this comes to 5°C per minute. The controller can be set to limit the heating rate.
2.13 Pressure
Work tubes are not able to accept high internal pressure. When gas seals or similar fittings are in
use, the gas pressure should be restricted to a maximum of 0.2 bar (3 psi). A pressure of about half
of that should normally be sufficient to achieve the desired flow rate. The customer must ensure
that the exhaust path from the tube is not blocked, so that excess pressure does not occur.
2.14 Thermocouples - Warnings
(1) The output from 1700-1800°C thermocouples when used regularly at temperatures greater than
1650°C can deteriorate and decrease with age.
Customers are advised periodically to check the thermocouple output, either by a calibration test,
or by comparing the output with a new reference thermocouple which has been subjected to high
temperatures for a minimum length of time.
Failure to check the thermocouple may result in overheating of the work and the furnace.
(2) The thermocouples fitted to these models give very low outputs below about 600°C, and do not
give accurate readings at low temperatures. The furnaces are not intended to be operated below
600°C.