Ivoclar Vivadent IPS InLine System - Manual (Page 25)

25
Shade adjustment with IPS InLine System Shade and Stains
These stains may be fired in a separate Stains firing. Minor shade adjustments and individual characterizations may also be
fired in the Glaze firing.
Dispense the desired quantity of IPS InLine System Shade and dilute and mix with IPS InLine System Glaze and Stains Liquid
to the desired consistency. Pooling should be avoided and the material must not be applied too thickly. If a more intensive
shade effect is desired, it is achieved by several staining procedures and repeated firing. The application of too many stains
results in an unnatural shade effect.
Glaze firing
After the Stains and Characterization firing with IPS InLine System Shade/Stains, the Glaze firing is conducted.
– If required, homogenize the Glaze paste by stirring it before taking it from its jar. Extrude the desired amount of
IPS InLine System Glaze paste from the syringe or jar and mix thoroughly on the mixing pad. If a different consistency is
desired, adjust the consistency by diluting the material with IPS InLine System Glaze and Stains Liquid. Next, apply the
Glaze material in the usual manner using a brush. Make sure not to apply the Glaze material either in too thick or too
thin layers.
– Minor shade adjustments may be carried out together with the Glaze firing.
Add-On after Glaze firing
Mix the IPS InLine System Add-On 690 °C/1274 °F material with the desired build-up liquid, apply on the missing areas,
and fire.
firing parameters for the IPS InLine System Shade/Stains firing (Stains and characterization firing)
T
°C/°F
B
°C/°F
S
min
t
°C/°F/min
H
min
V
1
°C/°F
V
2
°C/°F
850/1562 403/757 6 60/108 1 450/842 849/1560
firing parameters for the Glaze firing
T
°C/°F
B
°C/°F
S
min
t
°C/°F/min
H
min
V
1
°C/°F
V
2
°C/°F
850/1562 403/757 6 60/108 2 450/842 849/1560
firing paramters for the Add-On 690°c/1274°f after Glaze firing
T
°C/°F
B
°C/°F
S
min
t
°C/°F/min
H
min
V
1
°C/°F
V
2
°C/°F
690/1274 403/757 4 60/108 1 450/842 689/1272
Additional Stains and characterization firing cycles can be conducted with the same firing parameters.
When working with a furnace from other manufacturers these parameters have to be adjusted accordingly! Finally, the
shade of the completed restoration is checked.
IPS
InLine
One
–
One-Layer Metal-Ceramic
If less gloss is desired, the holding time can be reduced to 1 minute.
If the gloss is unsatisfactory after the first Glaze firing, further Glaze firing procedures
may be conducted using the same firing parameters.