Ivoclar Vivadent IPS e.max ZirPress - Manual (Page 74)

74
IPS e.max Ceram on IPS e.max ZirPress B S t ➚ T H V
1
V
2
L
Staining Technique °C/°F min. °C/°F/min °C/°F min. °C/°F °C/°F °C
ZirLiner firing – before wax-up and pressing 403/757 4:00 40/72 960/1760 1:00 450/842 959/1758 0
Stain and Characterization Firing 403/757 6:00 60/108 770/1418 1:00-2:00 450/842 769/1416 450/842
Glaze Firing 403/757 6:00 60/108 770/1418 1:00-2:00 450/842 769/1416 450/842
Add-On after Glaze Firing 403/757 6:00 50/90 700/1292 1:00 450/842 699/1290 450/842
IPS e.max Ceram on IPS e.max ZirPress/ZirCAD (Staining Technique)
IPS e.max Ceram on IPS e.max ZirPress B S t
➚
T H V
1
V
2
L
Cut-Back and Layering Technique °C/°F min. °C/°F/min °C/°F min. °C/°F °C/°F °C/°F
ZirLiner firing – before wax-up and pressing 403/757 4:00 40/72 960/1760 1:00 450/842 959/1758 0
Wash firing (foundation) 403/757 4:00 40/72 750/1382 1:00 450/842 749/1380 0
Wash firing (foundation) characterization 403/757 4:00 40/72 750/1382 1:00 450/842 749/1380 0
1 st Dentin / Incisal firing 403/757 4:00 40/72 750/1382 1:00 450/842 749/1380 0
2 nd Dentin / Incisal firing 403/757 4:00 40/72 750/1382 1:00 450/842 749/1380 0
Stain Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335 450/842
Glaze Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335 450/842
Add-On with Glaze Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335 450/842
Add-On after Glaze Firing 403/757 6:00 50/90 700/1292 1:00 450/842 699/1290 450/842
IPS e.max Ceram on IPS e.max ZirPress/ZirCAD (Cut-Back, Layering Technique)
Firing Parameters for IPS e.max ZirPress
– Use a honey-combed tray and the corresponding pins for firing.
– Ceramic pins must not be used, since they may fuse to the restoration.
– The processing temperatures must be observed. An increase in the firing temperature results in severe vitrification
between the framework and the veneering ceramic, which may lead to cracks later. An descrease in the firing
temperature causes the ceramic to be underfired and very brittle, which may lead to delamination.
– The parameters stipulated in the Instructions for Use are coordinated with Ivoclar Vivadent furnaces (tolerance range
+/- 10°C/18°F).
– If a non-Ivoclar Vivadent furnace is used, temperature corrections may be necessary.
– Remove IPS e.max ZirPress objects from the furnace after completion of the firing cycle (wait for the acoustic signal
of the furnace).
– Allow the objects to cool to room temperature in a place protected from draft.
– Do not touch the hot objects with metal tongs.
– Do not blast or quench the objects.