Ivoclar Vivadent IPS e.max CAD Labside - Manual (Page 64)

IPS e.max Ceram on IPS e.max CAD – Layering Technique
IPS e.max Ceram on IPS e.max CAD B S t
➚ T H V 1 V 2
Layering Technique °C/°F min. °C/°F/min °C/°F min. °C/°F °C/°F
Wash firing (foundation) 403/757 4:00 50/90 750/1382 1:00 450/842 749/1380
Wash firing (foundation) characterization 403/757 4:00 50/90 750/1382 1:00 450/842 749/1380
1. Dentin / Incisal Firing 403/757 4:00 50/90 750/1382 1:00 450/842 749/1380
2. Dentin / Incisal Firing 403/757 4:00 50/90 750/1382 1:00 450/842 749/1380
Stain Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335
Glaze Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335
Add-On with Glaze Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335
Add-On after Glaze Firing 403/757 6:00 50/90 700/1292 1:00 450/842 699/1290
IPS e.max Ceram on IPS e.max CAD-Cut – Back Technique
IPS e.max Ceram on IPS e.max CAD B S t
➚ T H V
1
V
2
Cut-Back Technique °C/°F min. °C/°F/min °C/°F min. °C/°F °C/°F
Wash firing (foundation) 403/757 4:00 50/90 750/1382 1:00 450/842 749/1380
Incisal firing 403/757 4:00 50/90 750/1382 1:00 450/842 749/1380
Stain firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335
Glaze firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335
Add-On with Glaze Firing 403/757 6:00 60/108 725/1337 1:00 450/842 724/1335
Add-On after Glaze firing 403/757 6:00 50/90 700/1292 1:00 450/842 699/1290
IPS e.max Ceram on IPS e.max CAD – Staining Technique
IPS e.max Ceram on IPS e.max CAD B S t ➚ T H V
1
V
2
Staining Technique °C/°F min. °C/°F/min °C/°F min. °C/°F °C/°F
Stain and Characterization firing 403/757 6:00 60/108 770/1418 1:00-2:00 450/842 769/1416
Glaze firing 403/757 6:00 60/108 770/1418 1:00-2:00 450/842 769/1416
Add-On after Glaze Firing 403/757 6:00 50/90 700/1292 1:00 450/842 699/1290
64
e.max
® CAD
–
Firing parameters
IP
S
– Use a honey-combed tray and the corresponding pins for firing.
– Ceramic pins must not be used, since they may fuse to the restoration.
– The processing temperatures must be observed. An increase in the firing temperature results in severe vitrification
between the framework and the veneering ceramic, which may lead to cracks later. An decrease in the firing
temperature causes the ceramic to be underfired and very brittle, which may lead to delamination.
– The parameters stipulated in the Instructions for Use are coordinated with Ivoclar Vivadent furnaces (tolerance range
+/- 10 °C).
– If a non-Ivoclar Vivadent furnace is used, temperature corrections may be necessary.
– Remove IPS e.max CAD objects from the furnace after completion of the firing cycle (wait for the acoustic signal of the
furnace).
– Allow the objects to cool to room temperature in a place protected from draft.
– Do not touch the hot objects with metal tongs.
– Do not blast or quench the objects.